AgNi-T Solid Contact Rivets

AgNi materials have higher resistance to arc erosion and contact welding than Ag or FAg.Both Properties are improved withincreasing Ni content. All AgNi materials show good workability and are easy to weld to contact supports. Low tendency towards material transfer in DC applications AgNi materials are environment-protective materials.

Materials:

AgNi10 AgNi15 AgNi20 AgNi-T AgNi30 AgNi40

General Description

Product Material

AgNi

Application Scope

AgNi contact materials find a wide range of application in Low voltge switching devies. They are used in power relays,small contactors,light switches,temperature controllers etc,as well as in protective switches (in the latter case they are used in asymmetric contact pairs, for instance,against AgC or AgZnO materials).

Material Characteristics

Tips	AgNi-T
Ni Content(wt.％)	12±1
Density(g/cm³)	≥10.20
Elec.Resistivity(µΩ•cm)	≤2.50
Hardness HV (Mpa)	≥600
Manufacturing process	Mixing-Compacting-Sintering

Wires	AgNi-T
Ni Content(Wt.％)	12±1
Density(g/cm³)	≥10.20
Elec.Resistivity(µΩ•cm)	≤2.05
Hardness HV (Mpa)	≥850
Tensile Strength(Mpa)	260-380
Elongation(％)	5-18
Manufacturing process	Sintering-Extrusion

Product Type

	AgNi-T
wires	√
Strips	√
Tips	√
Bimetal Strips	√
Rivets	√

Microstructure

AgNi-T 200X

Customised Presentation of Results

From off-standard sizes and shaped structures to special performance requirements, customers around the globe offer deeply customised metal stampings and electrical connection components.

→

←